Pengaruh Electroplating Krom Terhadap Ketebalan Dan Kekerasan Lapisan Pada Jari-Jari Sepeda Motor Yang Telah Di-Electroplating Nikel
Effect of Chrome Electroplating on The Thickness and Hardness of The Coating on The Spokes of a Motorcycle That Has Been Electroplated With Nickel
DOI:
https://doi.org/10.22236/metalik.v1i1.8459Keywords:
Electroplating; Thickness and Hardness; Nickel-Chrome CoatingAbstract
The purpose of this study was to determine the effect of chrome electroplating on the thickness and hardness of the spokes of a motorcycle wich has been electroplating nikel. This research was conducted in the laboratory room of PT. Enkei Indonesia and PT. Murni Cahaya Pratama Bekasi, West Java, Indonesia between January - March 2021 using nickel-chrome electroplating, the spokes of the motorcycle are made of st37 steel which has been electroplated with nickel, then electroplated with chrome. The parameters of the research were 4A, 6A, and 8A immersion currents. The tests carried out are thickness, hardness, macro structure and micro structure. The results showed that the effect of the strong current on the electroplating coating resulted in the highest value of thickness with an average of 26.77µm, the microstructure was corrosion resistant and non-magnetic, the macro structure showed the results of black spots indicating defects such as porosity and the highest value of hardness with an average 4H
Downloads
References
A Saleh, A. (2014). Electroplating Teknik Pelapisan Logam dengan Cara Listrik. Yrama Widya.
Afandi, Y. K., Arief, I. S., & Amiadji. (2015). Analisa Laju Korosi pada Pelat Baja Karbon dengan Variasi Ketebalan Coating. Jurnal Teknik Its, 4(1), 1–5.
Anton J. Hartomo & Tomijiro Kaneko. (1992). Mengenal Pelapisan Logam (Elektroplating).
Apriambudi, A. dwi. (2019). Pengaruh Variasi Waktu dan Konsetrasi Larutan terhadap Kekerasan Lapisan Nikel Electroplating Pada Baja Karbon Rendah. Skripsi.
Doloksaribu, M. (2017). Pengaruh Krom terhadap Sifat Mekanik dan Struktur Mikro pada Besi Cor Nodular 400. Metal Indonesia, 38(1), 8. https://doi.org/10.32423/jmi.2016.v38.8-13
Femiana Gapsari. (2017). Pengantar Korosi (Tim ub press (ed.)). Tim Ub Press.
HD, A. N. S., & Suheli. (2015). Sifat Fisis dan Mekanik Lapisan Nikel- Chromium pada Permukaan Baja Aisi 410. 48–54.
Kanani, N. (2004). Metal Finishing ” A Key Technology? Electroplating, 1–19. https://doi.org/10.1016/b978-185617451-0/50001-4
Kirono, S., & Purnomo, A. (n.d.). Analisa Karakteristik Material Spoke Wheel dengan Cast Wheel pada Pelek Sepeda Motor. 27–36.
Manurung, C. (2017). Pengaruh Kuat Arus terhadap Ketebalan Lapisan dan Laju Korosi (mpy) Hasil Elektroplating Baja Karbon Rendah dengan Pelapis Nikel.
Manurung, C., Pasar, M. J., Puri, K., & Sari, T. (2017). Pengaruh Kuat Arus terhadap Ketebalan Lapisan dan Laju Korosi (mpy) Hasil Elektroplating Baja Karbon Rendah dengan Pelapis Nikel. 45.
Meol, P. K., Maliwemu, E. U. K., Mesin, J. T., & Cendana, U. N. (2016). Pengaruh Tegangan Listrik Dan Waktu pada Krom Plating terhadap Keausan pada Hasil Produk Pengecoran Aluminium Scrap. 03(01), 47–54.
Nasution, D. I., & Sakti, A. M. (2018). Pengaruh Jarak Anoda Katoda dan Waktu Pencelupan pada Proses Pelapisan Nikel-Krom terhadap Ketebalan dan Kekerasan Lapisan Permukaan Knalpot Sepeda Motor. Jtm, 06(01), 41–49.
Noerochiem, L., Nurdiansah, H., & R, M. A. (2018). Pengaruh Variasi Waktu Pencelupan terhadap Ketebalan, Kekerasan dan Ketahanan Korosi Hasil Elektroplating Nikel-Hard Krom pada Baja AISI 4340. 7(2), 2301–9271.
Novianto, E. (2018). Studi Pelapisan Krom pada Baja Karbon dengan Arus 5 Ampere dan Variasi Tegangan 3, 6, 7.5, 9, 12 volt dengan Waktu Pencelupan 50 menit.
Pani, S. (2018). Pengaruh Variasi Kuat Arus Listrik dan Waktu Electroplating terhadap Ketebalan Lapisan Permukaan. Prinsip Dasar Electroplating Ahmad , 2011 . Prinsip dasar dari proses lapis listrik berpedoman atau berdasarka. 2(1), 18–25.
Prasetyo, S. D., Septe, E., & Mahyoeddin, J. (2015). Studi Korosi Temperatur Tinggi Baja ASSAB 760 di lingkungan Klor dan Sulfur. Jurnal Teknik Mesin.
Rasyad, A., & Arto, B. (2018). Analisis Pengaruh Temperatur, Waktu, dan Kuat Arus Proses Elektroplating terhadap Kekuatan Tarik, KRasyad, A., & Arto, B. (2018). Analisis Pengaruh Temperatur, Waktu, dan Kuat Arus Proses Elektroplating terhadap Kekuatan Tarik, Kekuatan Tekuk dan Kekerasa. Jurnal Rekayasa Mesin,
Saad, A., & Aguswendho. (2015). Karakteristik Pelapisan Krom terhadap Produk Logam sebagai upaya meningkatkan mutu di Sumatera Barat. Jurnal Teknik Mesin, 5(2), 83–87.
Setyahandana, B., & Christianto, Y. E. (2017). Pengaruh Hard Chrome Plating pada Peningkatan Kekerasan Baja Komponen Kincir. Jurnal Teknologi, 12(1), 26–35.
Subayu, R. D., & Sakti, A. M. (2018). Pengaruh Variasi Kuat Arus dan Tegangan Pada Proses Elektroplating Nikel Terhadap Ketebalan Permukaan dan Mampu Bending Knalpot Sepeda Motor. Jtm, 6(1), 121–128.
Sudana, I. M., Ida Ayu Anom Arsani, & Waisnawa, I. G. . S. (2014). Alat Simulasi Pelapisan Logam dengan Metode Elektroplating Simulation Tool With Metal Coating. Logic, 14(3), 190–198.
Sukarjo, H., & Pani, S. (2018). Pengaruh Variasi Kuat Arus Listrik dan Waktu Electroplating Nickel-Chrome terhadap Ketebalan Lapisan pada Permukaan Baja Karbon Rendah. Jurnal Engine, 2(1), 18–25.
Surya Darmawan, A. D., Dewa Ketut Okariawan, I., & Herlina Sari, N. (2015). Pengaruh Variasi Kuat Arus Listrik dan Waktu Proses Electroplating terhadap Kekuatan Tarik, Kekerasan dan Ketebalan 2 Lapisan pada Baja Karbon Rendah dengan Krom, The Influence Variation of Strong Electric Current Time and Process Electroplating Power of Att. Dinamika Teknik Mesin, 5(2), 66–71.
Yanto, D. D. (2018). Pengaruh Elektroplating Nikel terhadap Ketebalan Lapisan, Kekasaran, dan Kekerasan Permukaan Titanium dengan Variasi Waktu 20, 40, 60, 80 Menit. International Reviews of Immunology, 1–15. https://doi.org/10.3109/08830185.2014.902452